NORYL GTX™ GTX979 resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eGgzpG_NORYLGTXGTX979resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL GTX979 is a conductive, high heat material. It is especially designed for in- and on-line painted bodypanels and fenders in particular, with conductivity for electro-static painting in an unique way. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 15 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 11.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 1.2 - 1.6 | % | Internal method |
| Transverse flow : 3.20mm | 1.2 - 1.6 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 4.2 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2000 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 55.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 50.0 | MPa | ASTM D638 |
| Fracture | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/50 |
| Fracture 5 | 60 | % | ASTM D638 |
| Fracture | 30 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2050 | MPa | ASTM D790 |
| -- 7 | 2150 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 80.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | ISO 179/1eA |
| 23°C | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 150 | J/m | ASTM D256 |
| 23°C | 220 | J/m | ASTM D256 |
| -30°C 10 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 17 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 12 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 50.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 185 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span 13 | 178 | °C | ISO 75-2/Be |
| Vicat Softening Temperature | |||
| -- | 180 | °C | ASTM D1525, ISO 306/B50 10 14 |
| -- | 182 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 9.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 9.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 80°C | 9.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+3 - 1.0E+4 | ohms·cm | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (3.20 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 290 - 320 | °C | |
| Nozzle Temperature | 280 - 310 | °C | |
| Processing (Melt) Temp | 290 - 320 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.02 % |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 120*10*4 mm |
| 14 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ULTEM™ 2312EPR resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| ACCUTECH™ NY0730G20L | ACLO Compounders Inc. | Nylon 6 | ACCUTECH™ |
| Comai 600-4 BL | Comai Ltda | PP Homopolymer | Comai |
| Generic TPU-Polyether - Barium Sulfate | Generic | TPU-Polyether | Generic |
| Sylvin 9604-85 Clear Red 6254 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |