Zytel® 80G14AHS NC010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eGQGh6_Zytel-80G14AHS-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 14% Glass Reinforced, Toughened, Heat Stabilized, Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.19 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.70 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 2.00 mm, 50% RH) | 1.9 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5000 | 3300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 110 | 72.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.8 | 9.0 | % | ISO 527-2 |
| Flexural Modulus | 4400 | 3120 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | -- | 6.0 | kJ/m² | |
| -30°C | 9.0 | 7.0 | kJ/m² | |
| 23°C | 13 | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | -- | 71 | kJ/m² | |
| 23°C | 73 | 76 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 6.0 | -- | kJ/m² | |
| 23°C | 13 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 221 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | -- | °C | ISO 306/B50 |
| Melting Temperature 1 | 263 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 4.0E-5 | -- | cm/cm/°C | |
| Transverse | 1.2E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dissipation Factor (100 Hz) | 0.027 | 0.018 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (1.00 mm) | 44 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL NY66-IM2G33 | Polymer Resources Ltd. | Nylon 66 | PRL |
| UNIPURGE™ DFDB-0964 Natural 7 | The Dow Chemical Company | PE, Unspecified | UNIPURGE™ |
| NYCOA Polyamide 6115 HS | Nycoa (Nylon Corporation of America) | Nylon 612 | NYCOA Polyamide |
| Duratron® T5030 | Quadrant Engineering Plastic Products | PAI | Duratron® |
| LNP™ THERMOCOMP™ DZ004 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |