Chemlon® 233 GV
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eGO6ss_Chemlon-233-GV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Chemlon® 233 GV is a Polyamide 6 (Nylon 6) material filled with 33% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Chemlon® 233 GV: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.59 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.15 to 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.60 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 150 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 1.5 | % | |
| Break | 1.8 | % | |
| Flexural Modulus | 9480 | MPa | ASTM D790 |
| Flexural Strength | 203 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 208 | °C | ASTM D648 |
| Melting Temperature | 218 | °C | DSC |
| CLTE - Flow | 5.1E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+18 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 15 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | 300 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Oxygen Index | 33 | % | ASTM D2863 |
| FMVSS Flammability | PASSES | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 241 to 257 | °C | |
| Middle Temperature | 263 to 279 | °C | |
| Front Temperature | 263 to 285 | °C | |
| Nozzle Temperature | 263 to 285 | °C | |
| Processing (Melt) Temp | 263 to 285 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PP 30 GF FR0 NAT | RTP Company | PP, Unspecified | RTP |
| Nypol® PA A3 FR NTLA010 NR309 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| AKROMID® A3 S3 natural (1176) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| ESENTTIA 05C05 | Polipropileno del Caribe S.A. | PP Impact Copolymer | ESENTTIA |
| Plenco 07080 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |