Silamid® EF
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Roonamid a.s. |
| Trademark: | Silamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eG1kHt_Silamid-EF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, reduced flammability, high rigidity, shape stability, non halogenic flame retardant, natural, other color shades according to customer's requests, optimal processing properties. Suitable for injection mouldings in electrotechnics. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.19 | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | ||||
| Across Flow | 1.2 | 1.2 | % | |
| Flow | 1.3 | 1.3 | % | |
| Water Absorption (23°C, 24 hr) | 1.0 | 1.0 | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3500 | 1600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 60.0 | 30.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2800 | 1200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | 60 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 165 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | -- | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | -- | 4.60 | IEC 60250 | |
| Dissipation Factor (1 MHz) | -- | 0.12 | IEC 60250 | |
| Arc Resistance | 120 | -- | sec | ASTM D495 |
| Comparative Tracking Index (Solution A) | -- | 500 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | V-2 | -- | ||
| 3.20 mm | V-0 | -- | ||
| Glow Wire Ignition Temperature 1 | 960 | 960 | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 240 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Range: 850 to 960°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP792P | Southern Polymer, Inc. | HDPE | PRIMALENE |
| alphalon™ 40 | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
| Durethan® BG 30 X FN01 000000 | LANXESS Corporation | Nylon 6 | Durethan® |
| PolyBlend™ 1100 60A | CardioTech International, Inc. | PUR, Unspecified | PolyBlend™ |
| Hostacom X 4305 HL86 C1V301 | LyondellBasell Industries | PP Copolymer | Hostacom |