LNP™ STAT-LOY™ KX96821 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eDTmP1_LNP-STAT-LOY-KX96821-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY* KX96821 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Antistat. Also known as: LNP* STAT-LOY* Compound PDX-K-96821 Product reorder name: KX96821 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.9 | % | |
| Across Flow : 24 hr | 1.8 | % | |
| Water Absorption (24 hr, 50% RH) | 3.1 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1850 | MPa | ASTM D638 |
| -- | 1610 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 44.6 | MPa | ASTM D638 |
| Yield | 43.6 | MPa | ISO 527-2 |
| Break | 34.8 | MPa | ASTM D638 |
| Break | 39.5 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 15 | % | ASTM D638 |
| Yield | 12 | % | ISO 527-2 |
| Break | 54 | % | ASTM D638 |
| Break | 32 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1610 | MPa | ASTM D790 |
| -- | 1540 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 54.9 | MPa | ASTM D790 |
| -- | 40.6 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 2 | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 32.1 | J | ASTM D3763 |
| -- | 18.4 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 82.8 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 3 | 73.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.4E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.5E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 to 1.0E+11 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 188 to 199 | °C | |
| Front Temperature | 199 to 210 | °C | |
| Processing (Melt) Temp | 193 to 204 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TO 138 | Mitsubishi Chemical Performance Polymers, Inc. | SBS | tefabloc® |
| TEKNIFLEX® VPOA10200 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/EVOH/PE/PCTFE | TEKNIFLEX® |
| Sylvin 9812-80 Black | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Flontech® FT-905-DL | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| KOPLA PP KPT1020 | KOPLA Co., Ltd. | PP, Unspecified | KOPLA PP |