Ravago Compounds PP-6152
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Ravago Manufacturing Americas, LLC |
| Trademark: | Ravago Compounds |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eCEvP6_Ravago-Compounds-PP-6152.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Key Features:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 27 | g/10 min | ASTM D1238 |
| Ash Content | 22 | % | ASTM D2584 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 19.3 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 10 | % | ASTM D638 |
| Flexural Modulus - Tangent 1(23°C) | 1380 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Dart Drop Impact 2(23°C) | 11.3 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 101 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 57.2 | °C | ASTM D648 |
| CLTE - Flow | 2.3E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 93.3 | °C | |
| Drying Time | 0.0 - 8.0 | hr | |
| Rear Temperature | 177 - 216 | °C | |
| Middle Temperature | 177 - 216 | °C | |
| Front Temperature | 171 - 216 | °C | |
| Nozzle Temperature | 182 - 216 | °C | |
| Mold Temperature | 26.7 - 60.0 | °C | |
| Back Pressure | 0.00 - 0.689 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| Injection instructions |
|---|
| Hot Runner Temperature (if applicable): 380 to 450°F |
| Note Message | |
|---|---|
| 1 . | 0.050 mm/min |
| 2 . | Geometry GC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermylene® P8-32FG-2610 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| YUNGSOX® PP 1450D | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| AKROMID® B3 ICF 20 1 L black (5296) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| Luranyl® KR 2462 G2 | ROMIRA GmbH | PPE+PS | Luranyl® |
| 3M™ Dyneon™ Perfluoroelastomer PFE 40Z | 3M Advanced Materials Division | Perfluoroelastomer | 3M™ Dyneon™ Perfluoroelastomer |