PRL AC-GP1
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eBHD7y_PRL-AC-GP1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL AC-GP1 is a polyoxymethylene (POM) copolymer product,. It can be processed by extrusion or injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 - 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.8 - 2.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18mm | 61.4 | MPa | ASTM D638 |
| Fracture, 3.18mm | 61.4 | MPa | ASTM D638 |
| Flexural Modulus (3.18 mm) | 2600 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 90.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 69 | J/m | ASTM D256 |
| Dart Drop Impact (3.18 mm) | 22.6 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 157 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 110 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 - 85.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 168 - 174 | °C | |
| Middle Temperature | 179 - 185 | °C | |
| Front Temperature | 185 - 191 | °C | |
| Processing (Melt) Temp | 182 - 199 | °C | |
| Mold Temperature | 76.7 - 93.3 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 - 85.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 168 - 174 | °C | |
| Cylinder Zone 2 Temp. | 179 - 185 | °C | |
| Cylinder Zone 3 Temp. | 185 - 191 | °C | |
| Melt Temperature | 182 - 199 | °C | |
| Die Temperature | 76.7 - 93.3 | °C |
| Extrusion instructions |
|---|
| Drying Time: do not exceed 8 hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8602-70 Clear 893 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VITAMIDE® AI12WT6430 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| NORYL™ HS2000X resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| ADDINYL PMD 20143 | ADDIPLAST | Nylon 6 | ADDINYL |
| Polimid A 15 GF | Poliblend S.p.a. | Nylon 66 | Polimid A |