Order Products : sales@su-jiao.com
Lupoy® GN5001RFP
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e9Lv1f_Lupoy-GN5001RFP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupoy® GN5001RFP is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Lupoy® GN5001RFP are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 65.7 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 80 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2750 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 98.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 110 | °C | ASTM D648 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 85.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.20 mm | V-0 | ||
| 2.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 95.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 240 to 265 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 255 to 275 | °C | |
| Nozzle Temperature | 260 to 280 | °C | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Back Pressure | 0.0196 to 0.0588 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 陶氏低密度聚乙烯 218C | The Dow Chemical Company | LDPE | DOW™ LDPE |
| APEX® RE 8018 | Teknor Apex Company | PVC, Rigid | APEX® |
| GERMAMID 6.6 | Kunststoff-Kontor-Hamburg GmbH | Nylon 66 | GERMAMID |
| I. Stern 3320 | I. STERN & CO. INC. | PP Copolymer | I. Stern |
| Integra™ PA12 | PolySource, LLC | Nylon 12 | Integra™ |
