IPC PP 4825C-M
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | International Polymers Corporation |
| Trademark: | IPC PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e8g0vp_IPC-PP-4825C-M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IPC PP 4825C-M is a polypropylene copolymer material, which contains 25% mica filler. This product is available in North America,. The main characteristics of IPC PP 4825C-M are: copolymer. The typical application field of IPC PP 4825C-M is: automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.80 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 42.0 | MPa | ISO 527-2 |
| Flexural Modulus | 6200 | MPa | ISO 178 |
| Shear Modulus | 3300 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 2.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 105 | °C | ISO 75-2/A |
| Additional Information |
|---|
| The value listed as Shear Modulus, ASTM D732 was tested in accordance with ASTM D4065.Melt Mass-Flow Rate, ISO 1133, 230°C/2.16 kg: 10.0 to 14.0 g/10 minThe value listed as Molding Shrinkage, ISO 294-4 was tested in accordance with ISO 2577. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYLOY® MS-0020N-1 | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| Nypol® PA A3 V30 HL PRTA010 NR366 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Hiprolon® 200 VN LM | Arkema | Nylon 1010 | Hiprolon® |
| LNP™ LUBRICOMP™ UCL16AS compound | SABIC Innovative Plastics Europe | PPA | LNP™ LUBRICOMP™ |
| TECHNYL® B 230 GREY 1421 H | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® |