| DESCRIPTION: Epocast ® 1636-A/B epoxy syntactic is a high-performance, two-part system with high strength and good high temperature resistance. The aluminum-filled, medium-viscosity epoxy compound is easy to handle and machines easily in the cured state. Epocast ® 1636-A/B epoxy syntactic is used to reinforce honeycomb structures and is qualified to BMS 5-28, Type 6. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 1.07 | g/cm³ | ASTM D792 |
| -- | 1.72 | g/cm³ | ASTM D792 |
| -- 2 | 1.73 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Modulus | ASTM D695 | ||
| -- 3 | 276 | MPa | ASTM D695 |
| -- 4 | 3450 | MPa | ASTM D695 |
| -- 5 | 4140 | MPa | ASTM D695 |
| -- 6 | 5520 | MPa | ASTM D695 |
| Compressive Strength | |||
| -- 7 | 103 | MPa | ASTM D695 |
| -- 8 | 34.5 | MPa | ASTM D695 |
| -- 9 | 193 | MPa | ASTM D695 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability | Self Extinguishing | BSS 7230-F4 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time (25°C) 10 | 2.0 | hr | ASTM D2471 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time (25°C) | 7.0 | day | |
| Tensile Lap Shear - AL/AL | 13.8 | MPa | ASTM D1002 |
| Weight Gain 11 | ASTM D543 | ||
| Distilled Water : 25°C | % | ASTM D543 | |
| Mil-M-5606, hydraulic fluid : 25°C | % | ASTM D543 | |
| Skydol hydraulic fluid : 25°C | % | ASTM D543 | |
| TT-S-735, Type II test fluid : 25°C | % | ASTM D543 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 8.0 | ||
| Shelf Life (25°C) | 52 | wk | |
| Thermoset Mix Viscosity | ASTM D2196 | ||
| 25°C | 29000 | cP | ASTM D2196 |
| 25°C 12 | 1000 | cP | ASTM D2196 |
| 25°C 13 | 38000 | cP | ASTM D2196 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CURE SCHEDULE: 7 days at 77°F (25°C), or gel at 77°F (25°C) and raise temperature approximately 5-7°F (3-4°C) per minute to 260°F (127°C), hold 90 minutes, or 350F° (177°C), hold 60 minutes. |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Resin |
| 3 . | Tested at 350°F after 14 days at 350°F |
| 4 . | Tested at 77°F after 14 days at 350°F |
| 5 . | Room temperature gel plus 1 1/2 hrs at 250°F |
| 6 . | 7 days at 77°F |
| 7 . | 7 days at 77°F |
| 8 . | Tested at 350°F after 14 days at 350°F |
| 9 . | Room temperature gel plus 1 1/2 hrs at 250°F |
| 10 . | 50 gms |
| 11 . | 24 hrs |
| 12 . | Hardener |
| 13 . | Resin |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermoset Plastics 340 No.70 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| Unichem 8562 | Colorite Polymers | PVC, Unspecified | Unichem |
| Elvaloy® 4924 | DuPont Packaging & Industrial Polymers | TP, Unspecified | Elvaloy® |
| LEXAN™ 4504 resin | SABIC Innovative Plastics | PPC | LEXAN™ |
| Evoprene™ G 618 | Mexichem Specialty Compounds Inc. | TPE | Evoprene™ G |