NEXUS Reprocessed ABS Black Repro
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Nexus Resin Group, LLC. |
| Trademark: | NEXUS Reprocessed |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e89Vli_NEXUS-Reprocessed-ABS-Black-Repro.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NEXUS Reprocessed ABS Black Repro is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in North America for injection molding. Important attributes of NEXUS Reprocessed ABS Black Repro are:
|
| General Information | |
|---|---|
| Recycled Content |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| -- | 0.952 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 4.0 to 5.0 | g/10 min | ASTM D1238 |
| Spiral Flow | 86.4 | cm | |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.80 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2200 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 47.6 | MPa | ASTM D638 |
| Flexural Modulus 3 | 2410 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.8 mm Span) | 71.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 190 to 210 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C) | 3.39 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 93.9 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 81.1 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 85.0 | °C | |
| CLTE - Flow (-40 to 60°C) | 1.5E-4 | cm/cm/°C | ASTM E831 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 25 | ASTM D523 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (127°C, 1000 sec^-1) | 155 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 to 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Suggested Shot Size | 50 to 70 | % | |
| Rear Temperature | 193 to 238 | °C | |
| Middle Temperature | 210 to 249 | °C | |
| Front Temperature | 221 to 254 | °C | |
| Nozzle Temperature | 232 to 277 | °C | |
| Processing (Melt) Temp | 232 to 277 | °C | |
| Mold Temperature | 48.9 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rotec® ABS TS 25/02 | ROMIRA GmbH | ABS | Rotec® ABS |
| NEXT SIGNATURE ABS E35-100HG | NEXT Specialty Resins, Inc. | ABS | NEXT SIGNATURE |
| Kemcor LD 4203 | Qenos Pty Ltd | LDPE | Kemcor |
| OxyVinyls® 310 | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |
| Sylvin 8600-55 Blue 8360 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |