POLYfill PPH GF5015 PD2
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYfill |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e7gTya_POLYfill-PPH-GF5015-PD2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fibre-reinforced Chemically coupled |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3400 | MPa | ISO 178 |
| Flexural Stress | 92.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 138 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 120 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 110 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ K115HF | Mando Advanced Materials Co., Ltd. | PPS | SEPAZ™ |
| TEREZ PA 6.6 7500 GF 25 H | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Witcom PBT 6G/3L1 | Witcom Engineering Plastics B.V. | PBT | Witcom PBT |
| ACCUTECH™ CP0437M10CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| KPOL-NYLON K-NY66/21I | KPOL Chem Co. | Nylon 66 | KPOL-NYLON |