RAMSHINE PV300G6
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMSHINE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e6N7b3_RAMSHINE-PV300G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% GLASS-FIBER REINFORCED, HEAT RESISTANCE AND MINIMAL MOULD SHRINKAGE ABS FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 8.0 | g/10 min | ASTM D1238 |
| 300°C/1.2 kg | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.10 - 0.20 | % | ASTM D955 |
| -- | 0.10 - 0.20 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 0.12 | % | ASTM D570 |
| Saturated, 23°C | 0.12 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 115 | ASTM D785 | |
| R scale | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 90.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 8000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 115 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C | 8.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 101 | °C | ASTM D648, ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+18 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 200 - 220 | °C | |
| Middle Temperature | 205 - 220 | °C | |
| Front Temperature | 220 - 250 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 35.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C49C15 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Radiflam® A FR 308 NER | Radici Plastics | Nylon 66 | Radiflam® |
| Sarlink® TPE ML-1130B BLK X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| Sylvin 9463-80 Black | Sylvin Technologies Incorporated | PVC Alloy | Sylvin |
| DOW™ Electrical & Telecommunications DGDK-6862 NT | The Dow Chemical Company | HDPE | DOW™ Electrical & Telecommunications |