IROGRAN® A 98 E 4066
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e5PQqf_IROGRAN-A-98-E-4066.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 98 E 4066 is a thermoplastic polyester-polyurethane for injection molding applications. Additional characteristics of the product are very short cycle times and high dimensional stability. PERFORMANCE FEATURES
APPLICATIONS For the production of technical parts, wheels and rollers, coupling halfs, sprocket wheels, buffers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.22 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (190°C/21.6 kg) | 15.0 | cm³/10min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore A, Injection Molded | 97 | ASTM D2240, ISO 868 | |
| Shore D, Injection Molded | 49 | ASTM D2240 | |
| Shore D, Injection Molded | 59 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | 30 | mm³ | ISO 4649 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | DIN 53504 | ||
| 100% Strain | 14.0 | MPa | |
| 300% Strain | 25.0 | MPa | |
| Tensile Stress 4(Break) | 50.0 | MPa | DIN 53504 |
| Tensile Elongation 5(Break) | 530 | % | DIN 53504 |
| Tear Strength 6 | 140 | kN/m | ISO 34-1 |
| Compression Set 7 | ASTM D395, ISO 815 | ||
| 23°C, 24 hr | 30 | % | |
| 70°C, 24 hr | 45 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Hot Air Dryer | 80.0 to 90.0 | °C | |
| Drying Time | |||
| -- | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Dew Point | -30.0 | °C | |
| Rear Temperature | 175 to 195 | °C | |
| Middle Temperature | 175 to 195 | °C | |
| Front Temperature | 175 to 195 | °C | |
| Nozzle Temperature | 180 to 200 | °C | |
| Processing (Melt) Temp | 170 to 195 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 25.0 to 40.0 | °C | |
| Cylinder Zone 1 Temp. | 165 to 195 | °C | |
| Cylinder Zone 2 Temp. | 165 to 195 | °C | |
| Cylinder Zone 3 Temp. | 165 to 195 | °C | |
| Cylinder Zone 4 Temp. | 165 to 195 | °C | |
| Cylinder Zone 5 Temp. | 165 to 195 | °C | |
| Adapter Temperature | 175 to 195 | °C | |
| Die Temperature | 175 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Injection Molded |
| 4 . | Injection Molded |
| 5 . | Injection Molded |
| 6 . | Injection Molded |
| 7 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trilene® HE2.0TF | Chandra Asri Petrochemical | PP Homopolymer | Trilene® |
| Utomer UT356 | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyester | Utomer |
| DuraGrip® DGR 6165TR | Advanced Polymer Alloys | TPE | DuraGrip® |
| HiFill® PEEK CF30 A NAT | Techmer Engineered Solutions | PEEK | HiFill® |
| Kepital® TX-11H | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |