TOTAL Polypropylene PPC 5660
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e5B7VZ_TOTAL-Polypropylene-PPC-5660.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene PPC 5660 is heterophasic copolymer with a Melt Flow Index of 7 g/10min. Polypropylene PPC 5660 is characterized by a medium fluidity offering a combination of ease of processing and good manufactured article properties in applications ranging from household to industrial. Polypropylene PPC 5660 has been developed for the manufacture of garden furniture, battery cases and other articles requiring a combination of good stiffness and impact properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent Density | 0.53 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2 |
| Flexural Modulus | 1200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 6.0 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | ||
| -20°C | 5.5 | kJ/m² | |
| 23°C | 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 92.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 145 | °C | ISO 306/A50 |
| -- | 65.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ ATC-000/000 AS Natural | PolyOne Corporation | Acetal (POM) Copolymer | Stat-Tech™ |
| LNP™ THERMOCOMP™ 9X11428J compound | SABIC Innovative Plastics | PPS | LNP™ THERMOCOMP™ |
| Loyblend® YA-1201 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | ABS+PBT | Loyblend® |
| Lusin® Clean G 320 | Chem-Trend L.P. | Unspecified | Lusin® |
| LNP™ LUBRILOY™ D20009 compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |