Description SABIC® LDPE 2100TN30W is a grade with excellent toughness and outstanding biaxial shrink properties.The material contains Anti block, has a very low energy consumption during processing and has excellent draw down ability. Application SABIC® LDPE 2100TN30W is a heavy duty film grade suitable for applications like shrink hoods, industrial sacks, carrier bags and liners. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.33 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.40 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested 1 | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm, blown film | 190 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 190 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, blown film | 11.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm, blown film | 11.0 | MPa | ISO 527-3 |
| MD : 50 µm, blown film | 28.0 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 23.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | > 200 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | > 500 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown FIlm (50.0 µm) | 300 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking - Blown Film (50.0 µm) | 20 | g | Internal method |
| Re-blocking - Blown Film (50.0 µm) | 10 | g | Internal method |
| Tear Strength 2 | ISO 6383-2 | ||
| MD : 50.0 µm | 30.0 | kN/m | ISO 6383-2 |
| TD : 50.0 µm | 30.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 93.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.0 µm, Blown Film) | 18 | % | ASTM D1003A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Films have been produced on Kiefel IBC film blown line at 200 kg/h. Die size 200 mm, die gap of 0.8 mm. |
| Note Message | |
|---|---|
| 1 . | BUR 3 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VYTEEN ABS 2904 DX9 | Lavergne Group | ABS | VYTEEN |
| Yanshan PE 1F7B | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| Nylene® BX3WQ662(X) | Custom Resins Group | Nylon 6 | Nylene® |
| Badamid® LB70 GF40 TM-Z3 | Bada AG | Nylon 6 | Badamid® |
| Durethan® AKV 30 GIT H2.0 900116 | LANXESS GmbH | Nylon 66 | Durethan® |