Quadrant EPP Semitron® ESd 500HR
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e4h5Wf_Quadrant-EPP-Semitron-ESd-500HR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Quadrant EPP Semitron® ESd 500HR is a Polytetrafluoroethylene (PTFE) product filled with mica. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.30 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.00 mm | 0.030 | % | |
| Saturation, 23°C | 2.0 | % | |
| Water Absorption 1(23°C, 3.00 mm) | 4.0 | mg | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 10.0 mm) | 50 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1800 | MPa | ISO 527-2/1B/1 |
| Tensile Stress (Break) | 10.0 | MPa | ISO 527-2/1B/5 |
| Tensile Strain (Break) | 50 | % | ISO 527-2/1B/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 100 | °C | ISO 75-2/A |
| Continuous Use Temperature | |||
| -- 2 | 260 | °C | |
| -- 3 | 280 | °C | |
| Melting Temperature (DSC) | 327 | °C | |
| CLTE - Flow | |||
| 23 to 100°C | 1.0E-4 | cm/cm/°C | |
| 23 to 150°C | 1.0E-4 | cm/cm/°C | |
| > 150°C | 1.4E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 to 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+10 to 1.0E+12 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Oxygen Index | > 95 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Weight, 24 hrs |
| 2 . | 20000 hrs |
| 3 . | Short periods |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G15 272 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| NIMA NH PA66UT | Ovation Polymers Inc. | Nylon 66 | NIMA |
| BMC 810 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| ETILINAS BPD 4038 | POLYETHYLENE MALAYSIA SDN BHD | MDPE | ETILINAS |
| StarFlex® 7012-1001 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarFlex® |