LNP LUBRICOMP ECL36 is a compound based on Polyetherimide resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound ECL-4036 Product reorder name: ECL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.48 | g/cm³ | ASTM D792 |
| -- | 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.040 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 21600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 179 | MPa | ASTM D638 |
| Fracture | 160 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 1.7 | % | ASTM D638 |
| Fracture | 1.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 19200 | MPa | ASTM D790 |
| -- | 16000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 231 | MPa | ASTM D790 |
| -- | 210 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.39 | ASTM D3702 Modified | |
| With Self-Static | 0.48 | ASTM D3702 Modified | |
| Wear Factor - Washer | 31.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 1 | 5.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 270 | J/m | ASTM D4812 |
| 23°C 2 | 18 | kJ/m² | ISO 180/1U |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 - 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 - 354 | °C | |
| Middle Temperature | 354 - 366 | °C | |
| Front Temperature | 366 - 377 | °C | |
| Processing (Melt) Temp | 360 - 366 | °C | |
| Mold Temperature | 121 - 149 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Potomer SG3 | Shanghai Potomer International Trade Co., Ltd. | PVC, Flexible | Shanghai Potomer |
| TEREZ PPA 7500 GF 30 HY | TER HELL PLASTIC GMBH | PPA | TEREZ PPA |
| Zytel® FN727 NC010A | DuPont Performance Polymers | Nylon 6 | Zytel® |
| Aclon™ 3280 | Honeywell | PCTFE | Aclon™ |
| Lucent TPO TPO-10G | Lucent Polymers, Inc. | Polyolefin, Unspecified | Lucent TPO |