Osterlene® HB3553Z

Category:	HDPE , High Density Polyethylene
Manufacturer:	Osterman & Company
Trademark:	Osterlene®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	e4HvXI_OsterleneHB3553Z.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

HB3553 is a high density polyethylene copolymer developed for blow molding applications.

HB3553 is recommended for use in applications which require a combination of high top load strength and good environmental stress crack resistance (ESCR).

Osterlene HB3553 meets the requirements of the Food and Drug Administration, 21 CFR Section 177.1520. This regulation allows the use of this olefin polymer in "...articles or components of articles intended for use in contact with food." Specific limitations may apply. Contact your Osterman sales representative for more information.

General Information
Additive	Zinc Stearate
Features	High ESCR (Stress Cracking Resistance) High strength Copolymer
Agency Ratings	FDA 21 CFR 177.1520
Processing Method	Blow molding

Physical	Nominal Value	Unit	Test Method
Density	0.953	g/cm³	ASTM D4883
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.35	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance
F50	35.0	hr	ASTM D1693B
100% Igepal, F50	45.0	hr	ASTM D1693A

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	65		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield)	27.6	MPa	ASTM D638
Tensile Elongation ²(Break)	> 700	%	ASTM D638
Flexural Modulus - Tangent	1240	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	190	J/m	ASTM D256
Tensile Impact Strength	277	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	73.9	°C	ASTM D648
Brittleness Temperature	< -75.0	°C	ASTM D746
Vicat Softening Temperature	131	°C	ASTM D1525

Note Message
1 .	51 mm/min
2 .	51 mm/min

Resin Grade	Manufacturer	Category	Trademark
PRE-ELEC® PE 1291	Premix Oy	HDPE	PRE-ELEC®
SHIN-A SEY-175APM75	SHIN-A T&C	Epoxy	SHIN-A
AKROMID® A3 GF 50 natural (2423)	AKRO-PLASTIC GmbH	Nylon 66	AKROMID®
ASI POLYPROPYLENE 1500-01	A. Schulman Inc.	PP Impact Copolymer	ASI POLYPROPYLENE
Karina CLEAR PVC COMPOUND -E 80/206-IS-RG	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina