Auracell® H
| Category: | CA , Cellulose Acetate |
| Manufacturer: | Rotuba Extruders, Inc. |
| Trademark: | Auracell® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e3pHi1_Auracell-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Auracell® H is a Cellulose Acetate (CA) product. It can be processed by injection molding and is available in Europe or North America. Primary characteristic: eco-friendly/green. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 2.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 76 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 29.6 | MPa | |
| Break, 23°C | 40.0 | MPa | |
| Break, 70°C | 19.3 | MPa | |
| Tensile Elongation (Break) | 39 | % | ASTM D638 |
| Flexural Modulus | 1210 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 45.5 | MPa | ASTM D790 |
| Deformation Under Load | ASTM D621 | ||
| 50°C, 6.9 MPa | 1.00 | % | |
| 50°C, 14 MPa | 6.00 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 59 | J/m | |
| 23°C | 210 | J/m |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Aging - wt. lost, 72 hr (82°C) | 1.8 | wt% | ASTM D706 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flow Beginning Temperature | 155 | °C | ASTM D569 |
| Soluble Matter Loss | 0.30 | % | ASTM D570 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 2.0 | hr | |
| Dew Point | -40.0 to -28.9 | °C | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 204 to 216 | °C | |
| Front Temperature | 204 to 216 | °C | |
| Nozzle Temperature | 210 to 221 | °C | |
| Mold Temperature | 37.8 to 82.2 | °C | |
| Injection Pressure | 8.27 to 10.3 | MPa | |
| Back Pressure | 0.00 to 0.345 | MPa | |
| Vent Depth | 0.051 to 0.076 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V942 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Maxxam™ PPH-40C Nat | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| New-prene™ 7155 | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| DynaStat® 2257 | Polymer Dynamix | Nylon 12 | DynaStat® |
| Geon™ Specialty Suspension CG E 44 | Mexichem Specialty Resins, Inc. | PVC Homopolymer | Geon™ Specialty Suspension |