Laticonther 52/11 CP3/600 F3
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laticonther |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e2X3Sq_Laticonther-52-11-CP3-600-F3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High thermal conductivity product based on Polypropylene homopolymer (PPh). Special filler. Potentially suitable for food/medical contact application. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.90 to 1.4 | % | |
| Flow : 2.00 mm | 0.90 to 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 20.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 100 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 115 | °C | ISO 306/B50 |
| Thermal Conductivity | 4.0 | W/m/K | Internal Method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAISOX 3225 | Formosa Plastics Corporation | LLDPE | TAISOX |
| TOTAL Polypropylene PPH 4060 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| U-polymer LM-8503-10 | UNITIKA Plastics Division | Polyarylate | U-polymer |
| Nymax™ GF 1200 A 40 IM Black 13A | PolyOne Corporation | Nylon 66 | Nymax™ |
| JSR EPR EP24 | JSR Corporation | EPDM | JSR EPR |