DOWLEX™ 2740G (Tape)
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e2Ch6w_DOWLEX-2740G-Tape-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ 2740G Polyethylene Resin is a high performance linear low density polyethylene suitable for the production of tapes and monofilaments used in woven or knitted fabrics. Tapes and monofilaments made from this resin exhibit an excellent tenacity at the required elongation at break values. DOWLEX 2740G Polyethylene Resin can be extruded via the blowing or casting method and tapes can be manufactured using the tape or film stretching process. Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.940 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 2(190°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature 3 | 125 | °C | ASTM D1525 |
| Additional Information |
|---|
| 100 Tex 带子（铸造薄膜）： 带子拉伸比： 韧性：5 到 6 cN/dtex 伸长率：28 到 32% 薄膜拉伸工艺（吹塑薄膜）： 22 µm 薄膜 韧性：3.2 cN/dtex 伸长率：55% 28 µm 薄膜 韧性：3.4 cN/dtex 伸长率：56% 360 dtex 单丝： 韧性：6.7 cN/dtex 伸长率：33% 收缩性 (100°C)：3.8% |
| Extrusion instructions |
|---|
| 熔体温度： 吹塑薄膜生产线：200 至 230°C 铸造薄膜生产线：240 至 270°C 拉伸比： 薄膜拉伸加工：7 至 7.5:1 带子拉伸加工：6 至 8:1 单丝：8 至 9:1 |
| Note Message | |
|---|---|
| 1 . | Compression molding |
| 2 . | Compression molding |
| 3 . | Compression molding |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 6003-55A UV | RTP Company | TPE | RTP |
| Vi-Chem PVC V221-80E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Karina STRAW CPVC COMPOUND 790-38/23-CRPC (**) | Karina Ind. e Com. de Plásticos Ltda | CPVC | Karina |
| Karina IVORY PVC COMPOUND 105907-35/ 1-BY-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Tritan™ LX100 | Eastman Chemical Company | Copolyester | Tritan™ |