TECAFINE® HDPE
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Ensinger Inc. |
| Trademark: | TECAFINE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dxW7CR_TECAFINE-HDPE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ASTM D1505 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 54 | ASTM D785 | |
| Durometer Hardness (Shore D) | 67 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 586 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 23.4 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | > 100 | % | ASTM D638 |
| Flexural Modulus (23°C) | 827 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 26.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 23.9 | °C | ASTM D648 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 |
| Service Temperature | |||
| Long Term Max. | 120 | °C | |
| Long Term Min. | -100 | °C |
| Additional Information |
|---|
| Data is obtained from extruded shapes material unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex GC-0703 | SAMSUNG SDI CO., LTD. | ABS+PET | Starex |
| Calprene® H6120 | Dynasol Elastomers | SEBS | Calprene® |
| EcoPaXX® Q170E | DSM Engineering Plastics | Nylon 410 | EcoPaXX® |
| Karina BLACK PVC COMPOUND 70900-48/1-H-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupoy® GN2101FC | LG Chem Ltd. | PC | Lupoy® |