Borealis PP MG160AI
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dx6bi8_Borealis-PP-MG160AI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MG160AI is a 10% mineral filled high crystallinity polypropylene compound intended for injection moulding. This material has an excellent balance between impact strength and stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.985 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.2 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 75.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (1.00 mm) | 1950 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 3.5 | % | ISO 527-2 |
| Flexural Modulus 1 | 1950 | MPa | ISO 178 |
| Flexural Stress | 36.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 3.5 | kJ/m² | ISO 179/1eA |
| 23°C | 7.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 80 | kJ/m² | ISO 179/1eU |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C | 3.5 | kJ/m² | ISO 180/1A |
| 23°C | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -20°C | 60 | kJ/m² | ISO 180/1U |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A |
| -- | 70.0 | °C | ISO 306/B |
| CLTE - Flow (80°C) | 7.8E-5 | cm/cm/°C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperature: 40 - 80 °CMass Tmperature: 230 - 280 °CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 807 TFE 15 | RTP Company | Acetal (POM) Copolymer | RTP |
| Aaron AVPE LD 300-1 | Aaron Industries Corp. | LDPE | Aaron |
| Crastin® SK615SF NC010 | DuPont Performance Polymers | PBT | Crastin® |
| IDI SMC E-204 | IDI Composites International | TS, Unspecified | IDI SMC |
| InnoTooling™ IE-644-08 | Innovative Polymers, Inc. | TSU | InnoTooling™ |