LNP™ LUBRICOMP™ EL003 compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dwsHE6_LNPLUBRICOMPEL003compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound EL-4030 Product reorder name: EL003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.80 - 1.1 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.80 - 1.1 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.21 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.25 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2760 | MPa | ASTM D638 |
| -- | 2740 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 88.7 | MPa | ASTM D638 |
| Yield | 83.0 | MPa | ISO 527-2 |
| Fracture | 85.2 | MPa | ASTM D638 |
| Fracture | 82.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 6.5 | % | ASTM D638 |
| Yield | 6.3 | % | ISO 527-2 |
| Fracture | 10 | % | ASTM D638 |
| Fracture | 8.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2900 | MPa | ASTM D790 |
| -- | 3020 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 136 | MPa | ASTM D790 |
| -- | 130 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.30 | ASTM D3702 Modified | |
| With Self-Static | 0.23 | ASTM D3702 Modified | |
| Wear Factor - Washer | 106 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 69 | J/m | ASTM D256 |
| 23°C 2 | 8.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 750 | J/m | ASTM D4812 |
| 23°C 3 | 62 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 9.60 | J | ASTM D3763 |
| -- | 1.48 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 182 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 182 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 4.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 - 354 | °C | |
| Middle Temperature | 354 - 366 | °C | |
| Front Temperature | 366 - 377 | °C | |
| Processing (Melt) Temp | 360 - 366 | °C | |
| Mold Temperature | 121 - 149 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4004 | RTP Company | PPA | RTP |
| Sylvin 5137-94 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Taitacell EPS 321S | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| GLAMIDE® NB-1700 | TOYOBO America, Inc. | Nylon, Unspecified | GLAMIDE® |
| Karina LIGHT BLUE PVC COMP. -E600D06/958 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |