Order Products : sales@su-jiao.com
Geon™ HTX M6215
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ HTX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dvUcBC_Geon-HTX-M6215.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Geon™HTX M6215 is a polyvinyl chloride alloy (PVC alloy) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Geon™The application areas of HTX M6215 include the automotive industry, electrical/electronic applications, electrical appliances, wires and cables, and construction applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Spiral Flow | 86.4 | cm | |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2340 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 44.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 60 | % | ASTM D638 |
| Flexural Modulus | 2390 | MPa | ASTM D790 |
| Flexural Strength | 73.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256A | ||
| 0°C, 3.18mm, injection molding | 160 | J/m | ASTM D256A |
| 23°C, 3.18mm, injection molding | 270 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.35mm | 77.8 | °C | ASTM D648 |
| 0.45 MPa, annealed, 6.35mm | 87.2 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.35mm | 72.8 | °C | ASTM D648 |
| 1.8 MPa, annealed, 6.35mm | 85.0 | °C | ASTM D648 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm, ALL) | V-0 5VA | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| CSA Flammability 4(1.60 mm) | 5VA V-0 | ||
| It is recommended that the compound pellets be dried for 3 to 4 hours at 150 deg. F. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 202 - 210 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Type 1, 5.1 mm/min |
| 4 . | All colors |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 841 DEL | RTP Company | Acetal (POM) Homopolymer | RTP |
| RheTech Polypropylene G40P100-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| UNISOFT ADHESION™ AD-55A-NT-1-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT ADHESION™ |
| Envir® PA6N3L-BK0305 | Barnet | Nylon 6 | Envir® |
| OMIKRON BE 937 NAT | TECNOPOL | PP Homopolymer | OMIKRON |