TRIEL® 5206SP
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | Samyang Corporation |
| Trademark: | TRIEL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dtglnY_TRIEL-5206SP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIEL® 5206SP is a Thermoplastic Polyester Elastomer (TPEE) product. It is available in Asia Pacific, Europe, or North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 to 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 to 1.7 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 20 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Break | 6.86 | MPa | |
| 5.0% Strain | 0.981 | MPa | |
| 10% Strain | 2.45 | MPa | |
| 50% Strain | 3.92 | MPa | |
| Tensile Elongation (Break) | > 400 | % | ASTM D638 |
| Flexural Modulus | 16.7 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 1.77 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | ASTM D256 | ||
| -40°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 43.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 65.0 | °C | ASTM D1525 1 |
| Melting Temperature | 170 | °C | ASTM D2117 |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer FEA-241U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| BMC 3001 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Formolene® 4100N | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| KPOL-HDPE HD K-I 8/962 | KPOL Chem Co. | HDPE | KPOL-HDPE |
| EPAMOULD 655D55 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |