LNP™ LUBRILOY™ RF208 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dsqQwI_LNPLUBRILOYRF208compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* RF208 is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Lubricant. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRILOY* Compound RF-40 Product reorder name: RF208 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.40 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.1 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.1 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.41 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.28 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.40 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12300 | MPa | ASTM D638 |
| -- | 10500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 139 | MPa | ASTM D638 |
| Fracture | 137 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.5 | % | ASTM D638 |
| Fracture | 2.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9030 | MPa | ASTM D790 |
| -- | 11300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 200 | MPa | ASTM D790 |
| -- | 211 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.41 | ASTM D3702 Modified | |
| With Self-Static | 0.30 | ASTM D3702 Modified | |
| Wear Factor - Washer | 54.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 2 | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 720 | J/m | ASTM D4812 |
| 23°C 3 | 56 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.6 | J | ASTM D3763 |
| -- | 3.59 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 242 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 238 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 271 - 282 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BMN P40 D | Arkema | Nylon 11 | Rilsan® |
| Titanvene™ LL0220SR | PT. TITAN Petrokimia Nusantara | LLDPE | Titanvene™ |
| Epic Urethane S7253 | Epic Resins | PUR, Unspecified | Epic Urethane |
| Hostaform® CF802 10/9022 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| 3M™ Dyneon™ Fluoroelastomer FE 5530 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |