Envir® PA66G15THL-BK0101
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Barnet |
| Trademark: | Envir® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dsfWuz_Envir-PA66G15THL-BK0101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Envir® PA66G15THL-BK0101 is a 15% Glass fiber reinforced Nylon 66 molding resin that is also highly Toughened. 66G15THL-BK0101 is Heat stabilized and hydrolysis resistant, it is optimized for strength and impact properties while giving excellent processibility. It is provided Black in color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (280°C/2.16 kg) | 15.0 | cm³/10min | ASTM D1238 |
| Ash Content | 15 | % | ASTM D5630 |
| Moisture Content | < 0.20 | % | ASTM D6980 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Granularity | 3.40 | g/100 pellets |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5780 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 110 | MPa | |
| Break | 108 | MPa | |
| Tensile Strain (Break) | 4.5 | % | ISO 527-2 |
| Flexural Modulus | 5330 | MPa | ISO 178 |
| Flexural Stress | 185 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 15 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | 60 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 260 | °C | ASTM D3418 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| megol® HT SV/P 85 | API SpA | SEBS | megol® |
| Hylon® N2033STHL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| Lupoy® GP1000MD | LG Chem Ltd. | PC | Lupoy® |
| LEXAN™ ML7667 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| VALOX™ 310SE0 resin | SABIC Innovative Plastics | PBT | VALOX™ |