Hytrel® HTR8341G BK320
| Category: | TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dsSEAa_Hytrel-HTR8341G-BK320.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40 Shore D, Slightly Lubricated, High Viscosity Polyester Elastomer with Superior Fatigue Resistance Developed for Blow Molding |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 1.00 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.50 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 40 | ||
| Shore D, 15 sec | 37 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 80.0 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 29.0 | MPa | |
| 10% Strain | 6.70 | MPa | |
| 50% Strain | 11.9 | MPa | |
| Tensile Strain (Break) | > 300 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 390 | % | ISO 527-2 |
| Flexural Modulus | 80.0 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 34-1 | ||
| Across Flow | 120 | kN/m | |
| Flow | 110 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, Partial Break | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 208 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.8E-4 | cm/cm/°C | |
| Transverse | 1.7E-4 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1022HS | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| CELLOMER® 2100D | Microcell Composite Company | SBS | CELLOMER® |
| FHR Polypropylene P6G2N-095 | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Laticonther 52/11 GR/70 | LATI S.p.A. | PP Homopolymer | Laticonther |
| Hypro® PP-HP 35NS | Entec Polymers | PP Homopolymer | Hypro® |