Order Products : sales@su-jiao.com
LNP™ THERMOCOMP™ RF00ASXZ compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | drYdnt_LNP-THERMOCOMP-RF00ASXZ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOCOMP* RF00ASXZ is a compound based on Nylon 66 resin containing 50% Glass Fiber. Added feature of this material is: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound RF-100-10 HS Product reorder name: RF00ASXZ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.59 | g/cm³ | |
| -- | 1.58 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.41 | % | |
| Across Flow : 24 hr | 1.1 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.48 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.77 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 16400 | MPa | ASTM D638 |
| -- | 15800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 188 | MPa | ASTM D638 |
| Break | 185 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.8 | % | ASTM D638 |
| Break | 1.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 14800 | MPa | ASTM D790 |
| -- 5 | 14400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 272 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 281 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 97 | J/m | ASTM D256 |
| 23°C 7 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 820 | J/m | ASTM D4812 |
| 23°C 8 | 52 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 8.70 | J | ASTM D3763 |
| -- | 2.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 257 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 256 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 248 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 247 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALAT 9383GFR300 | AD majoris | PBT | MALAT |
| Retpol® 1210 TF HS UV3 | PolyPacific Pty. Ltd. | PP Copolymer | Retpol® |
| Shandong PA1212 A3S01 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| Multilon® T-2850R | TEIJIN LIMITED | PC+ABS | Multilon® |
| ECOLEN® HZ40L | HELLENIC PETROLEUM S.A. | PP Homopolymer | ECOLEN® |