Heramid® S NER GFP 3010
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Radici Plastics |
| Trademark: | Heramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dp7frS_Heramid-S-NER-GFP-3010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA6 30% glass fiber and mineral filler reinforced injection moulding grade. Black colour. Post-industrial grade produced with selected polymers coming from polymerization, fibres and compounding plants. ISO 1043 : PA6 (GF+MX)30 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 85.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 6400 | MPa | ISO 178 |
| Flexural Stress 2 | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 190 | °C | ISO 75-2/Af |
| Melting Temperature 3 | 222 | °C | ISO 11357 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUCLAIR® MB509H | SK Global Chemical | MDPE | YUCLAIR® |
| alphalon™ 27 | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
| ESTASTIR HI 10 V0 | Cossa Polimeri S.r.l. | PS (HIPS) | ESTASTIR |
| Latistat 48/9900-03 | LATI S.p.A. | EVA | Latistat |
| Plenco 04599 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |