Nycal™ 2155R13
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Technical Polymers, LLC |
| Trademark: | Nycal™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | doyQcL_Nycal-2155R13.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nycal™2155R13 is a polyamide 66 (nylon 66) material, which contains a 13% glass fiber reinforced material. This product is available in North America and is processed by injection molding. Nycal™The main characteristics of 2155R13 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 114 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 4830 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 241 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 224 | °C | ASTM D648 |
| Melting Temperature | 257 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Tensile Elongation, ASTM D638: 2 to 4%Volum Resistivity, ASTM D257: >1e14 ohm-cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.9 - 79.4 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 271 - 299 | °C | |
| Mold Temperature | 65.6 - 98.9 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech T9703 | Shanghai Suptech Engineering Plastics Co. Ltd. | PBT | Sup-tech |
| BESTPOLUX PCG2X/02 | Triesa Plastics | PC | BESTPOLUX |
| Allen ABS 552/499 | SEKISUI Polymer Innovations, LLC | ABS | Allen ABS |
| Huafon JF-HSY-ADP2 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Karina CLEAR PVC COMPOUND 74/203-D-IS-SI (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |