PETLIN LD N119X
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | PETLIN (MALAYSIA) SDN BHD |
| Trademark: | PETLIN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dogSPl_PETLIN-LD-N119X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETLIN LD N119X is a low density polyethylene resin designed for a wide range of applications. It is produced by the state-of-the-art DSM Stamicarbon tubular process. It contains antioxidant (BHT free) additives. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.9 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance | 70.0 | hr | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 50 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 175 | MPa | ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 89.0 | °C | ISO 306 |
| Melting Temperature (DSC) | 108 | °C | DIN 53765 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 58 | ASTM D2457 | |
| Haze | 8.3 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 170 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mowiol® 6-98 | Kuraray Co., Ltd. | PVOH | Mowiol® |
| Xuchuan 6180/B-8280 (Sole) | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Adell Polyamide AR-77 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| APEX® 3211-85NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Kingfa MAC-601 AC | Kingfa | PC+ABS | Kingfa |