NORYL™ WCV065 resin
| Category: | PPE+Polyolefin , Polyphenylene Ether + Polyolefin |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dh8qTX_NORYL-WCV065-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flexible, non-halogenated FR, PPE+Polyolefin resin designed for evaluation in Automotive ISO6722 Class A-C applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 20 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 20.9 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shao D, 30 seconds) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1450 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 1 | 37.0 | MPa | ASTM D638 |
| Yield | 39.0 | MPa | ISO 527-2/50 |
| Fracture 2 | 37.0 | MPa | ASTM D638 |
| Fracture | 37.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 3 | 37 | % | ASTM D638 |
| Yield | 17 | % | ISO 527-2/50 |
| Fracture 4 | 45 | % | ASTM D638 |
| Fracture | 38 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 5 | 1150 | MPa | ASTM D790 |
| -- 6 | 1260 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 44.0 | MPa | ISO 178 |
| Yield, 50.0mm span 7 | 41.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 8(23°C) | 43 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 550 | J/m | ASTM D256 |
| -30°C 9 | 9.0 | kJ/m² | ISO 180/1A |
| 23°C 10 | 41 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 42.0 | J | ASTM D3763 |
| 23°C, Total Energy | 33.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 115 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 84.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 11 | 93.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 71.0 | °C | ASTM D1525, ISO 306/B50 9 12 |
| -- | 76.0 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 8.2E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 1.3E-4 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Permittivity (1 MHz) | 2.55 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 2.0E-3 | IEC 60250 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 210 - 260 | °C | |
| Cylinder Zone 3 Temp. | 230 - 285 | °C | |
| Cylinder Zone 5 Temp. | 250 - 285 | °C | |
| Melt Temperature | 250 - 285 | °C | |
| Die Temperature | 250 - 285 | °C |
| Extrusion instructions |
|---|
| Conductor Pre-heat Temperature: 80 - 150 °CCooling Water Air Gap: 100 - 200 mmCross-head Temperature: 250 - 285 °CDrying Time (Cumulative): 12 hrsExtruder Length/Diameter Ratio (L/D): 22:1 to 26:1Neck Temperature: 250 - 285 °CScreen Pack: 150 - 100Screw Speed: 15 - 40 rpmWater Bath Temperature: 15 - 80 °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 sp=62mm |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® STR 1032EU-01 NATURAL | A. Schulman Inc. | Polyolefin, Enhanced TPO | POLYTROPE® |
| Starex NH-0825 | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Ultralloy™ 40 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| Buna® EP T 2450 | LANXESS Corporation | EPDM | Buna® EP |
| InnoTooling™ IE-644-04 | Innovative Polymers, Inc. | TSU | InnoTooling™ |