PRIMACOR™ 1410
| Category: | EAA , Copolymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | PRIMACOR™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dgZY09_PRIMACOR-1410.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRIMACOR™1410 copolymer is an ethylene acrylic acid copolymer, suitable for single-layer or co-extrusion blown films. PRIMACOR 1410 copolymer is specially used as heat seal layer or adhesive layer in composite film. PRIMACOR 1410 copolymer has the following characteristics:
Application field:
Meet the following regulatory requirements:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.938 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) 1(190°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238, ISO 1133 |
| Comonomer Content 2 | 9.7 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, molding 3 | 8.39 | MPa | ASTM D638 |
| Yield, molding | 8.39 | MPa | ISO 527-2/508 |
| Fracture, molding 4 | 22.5 | MPa | ASTM D638 |
| Fracture, molding | 22.5 | MPa | ISO 527-2/508 |
| Tensile Elongation | |||
| Fracture, molding 5 | 640 | % | ASTM D638 |
| Fracture, molding | 640 | % | ISO 527-2/508 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| MD : Yield, 51 µm | 11.8 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 10.9 | MPa | ASTM D882 |
| MD : Yield, 51 µm | 11.8 | MPa | ISO 527-3 |
| TD : Yield, 51 µm | 10.9 | MPa | ISO 527-3 |
| MD : Fracture, 51 µm | 37.9 | MPa | ASTM D882, ISO 527-3 |
| TD : Fracture, 51 µm | 38.1 | MPa | ASTM D882, ISO 527-3 |
| Tensile Elongation | ASTM D882, ISO 527-3 | ||
| MD : Fracture, 51 µm | 400 | % | ASTM D882, ISO 527-3 |
| TD : Fracture, 51 µm | 470 | % | ASTM D882, ISO 527-3 |
| Dart Drop Impact (51 µm) | 580 | g | ASTM D1709B, ISO 7765-1/B |
| Elmendorf Tear Strength 6 | |||
| MD : 51 µm | 380 | g | ASTM D1922 |
| TD : 51 µm | 510 | g | ASTM D1922 |
| MD : 51 µm | 1700 | N | ISO 6383-2 |
| TD : 51 µm | 2300 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 81.1 | °C | ASTM D1525, ISO 306 |
| Melting Temperature (DSC) | 97.8 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 65 | ASTM D2457 | |
| Haze | |||
| 50.8 µm | 5.8 | % | ISO 14782 |
| 50.8 µm | 5.8 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 薄膜的制造条件：用于处理此树脂的设备应由耐腐蚀材料制成。建议模具和适配器采用不锈钢和/或双面镀铬或镀镍。 螺杆尺寸：2.5 英寸 (63.5 mm)；30:1 L/D 螺杆类型：带 Maddock Mixer 的单跨型 模具间隙：40 密尔 (1.0 mm) 熔体温度：385°F (196°C) 输出：模具周长的 6 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 冷冻线高度：29 英寸 (737 mm) |
| Note Message | |
|---|---|
| 1 . | As measured during production. |
| 2 . | The comonomer content measured by Dow attribute method has the same accuracy as ASTM D 4094. |
| 3 . | 510 mm/min |
| 4 . | 510 mm/min |
| 5 . | 510 mm/min |
| 6 . | The crosshead speed is 20 inches per minute. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® 22LHI6 XE-NBK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| NYCOA Polyamide 7550 Nat | Nycoa (Nylon Corporation of America) | Nylon 12 | NYCOA Polyamide |
| Hanwha Total PE R902P | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |
| Polychim HA31XTF | Polychim Industrie S.A.S. | PP Homopolymer | Polychim |
| Celanex® 5206HG | Celanese Corporation | PET | Celanex® |