PRE-ELEC® PE 1296
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | delE0b_PRE-ELEC-PE-1296.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PE 1296 is a conductive thermoplastic concentrate based on PE-HD. Conductivity is achieved by using a special conductive carbon black. PRE-ELEC® PE 1296 contains a high load of carbon black and it can be diluted up to 50% with virgin or recycled PE-HD. The actual amount should always be tested as it also depends on the processing conditions. Typical applications for PRE-ELEC® PE 1296 include blow moulded canisters and containers and mono- or co-extruded pipes and sheets. It can also be used in injection molding. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.11 | g/cm³ | ASTM D792 |
| -- | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 0.60 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 2.5 - 3.5 | % | ASTM D955 |
| Flow direction | 2.5 - 3.5 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw A | 95 | ISO 868 | |
| Shaw D | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 24.0 | MPa | ISO 527-2 |
| -- | 13.1 | MPa | ASTM D638 |
| 4.00 mm | 13.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 12 | % | ISO 527-2 |
| Fracture, 4.00mm | 40 | % | ISO 527-2 |
| Flexural Modulus (4.00 mm) | 1200 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1 | |||
| -20°C | 61 | kJ/m² | ASTM D256 |
| -20°C | 60 | kJ/m² | ISO 179 |
| 23°C | 65 | kJ/m² | ISO 179 |
| 23°C | 67 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | |||
| -20°C | No Break | ASTM D256, ISO 179 | |
| 2°C | No Break | ISO 179 | |
| 23°C | No Break | ASTM D256 | |
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | 60.9 | kJ/m² | ASTM D256 |
| 23°C, 4.00 mm | 73.6 | kJ/m² | ASTM D256 |
| Notched Izod Impact 3 | ISO 180 | ||
| -20°C | 60 | kJ/m² | ISO 180 |
| 23°C | 71 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ASTM D256 | |
| 23°C, 4.00 mm | No Break | ASTM D256 | |
| Unnotched Izod Impact Strength 4 | ISO 180 | ||
| -20°C | No Break | ISO 180 | |
| 23°C | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 76.7 | °C | ASTM D648B |
| 0.45 MPa, not annealed | 77.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 43.3 | °C | ASTM D648A |
| 1.8 MPa, not annealed | 43.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 76.1 | °C | ASTM D1525 5 |
| -- | 129 | °C | ASTM D1525, ISO 306/A50 5 6 |
| -- | 73.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+5 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+3 | ohms·cm | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 60.0 - 80.0 | MPa | |
| Injection Rate | Moderate |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 200 | °C | |
| Cylinder Zone 2 Temp. | 210 | °C | |
| Cylinder Zone 3 Temp. | 220 | °C | |
| Cylinder Zone 4 Temp. | 220 | °C | |
| Cylinder Zone 5 Temp. | 230 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 230°C |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| 3 . | 4 mm thick |
| 4 . | 4 mm thickness |
| 5 . | 标准 B (120°C/h), 载荷2 (50N) |
| 6 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SFR5800C2 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| TECHLEN M1600 | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| Sylvin 2973-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LG ASA LI931-C | LG Chem Ltd. | ASA | LG ASA |
| LNP™ STAT-KON™ DEL22P compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |