UNIVAL™ DMDA-6400 NT 7
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | UNIVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | deS26A_UNIVAL-DMDA-6400-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UNIVAL™DMDA-6400 NT 7 is a multi-purpose HDPE homopolymer used in blow molding containers for dairy products, water and fruit juice drinks. Its products have high stiffness, excellent odor and taste characteristics, and can be used to make special white plastic bottles. This resin can be used in the manufacture of food packaging and household articles with thin-walled structures by blow molding or thermoforming. Main features:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.961 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.80 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 57 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 20.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 66 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 32.0 | MPa | ASTM D638 |
| Fracture | 24.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 1000 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 1300 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 84.0 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 76.0 | °C | ASTM D648 |
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 131 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 133 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 120 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行基板模制和测试。 |
| Note Message | |
|---|---|
| 1 . | Type s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makroblend® AR205 | Covestro - Polycarbonates | PC+PET | Makroblend® |
| Unipren® Elastomers A3 PRTA010 65A IM06S1 UP338 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| NEXT REGRIND PET 530-300RG | NEXT Specialty Resins, Inc. | PET | NEXT REGRIND |
| DESLOY™ DSC891A | DESCO Co., Ltd. | PC+ABS | DESLOY™ |
| OTECH PVC OM5519-Sandal | OTECH Corporation | PVC, Unspecified | OTECH PVC |