HOPELEX LX-7603
| Category: | PC , Polycarbonate |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | HOPELEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ddr7A9_HOPELEX-LX-7603.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High impact strength Non-brominated, non-chlorinated flame retardant Diffusion plate, diffusion profile and finishing materials |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 59.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 100 | % | ASTM D638 |
| Flexural Modulus 3 | 2260 | MPa | ASTM D790 |
| Flexural Strength 4(Yield) | 87.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 740 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 129 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 70.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 290 to 310 | °C | |
| Middle Temperature | 280 to 300 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 280 to 300 | °C | |
| Processing (Melt) Temp | 290 to 310 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 238 V13 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| XYRON™ X332V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Xuchuan XCW-8060DY | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Hostacom X 454 | LyondellBasell Industries | PP Copolymer | Hostacom |
| LEXAN™ 4504 resin | SABIC Innovative Plastics | PPC | LEXAN™ |