Hyrene® PS-HI 3/4
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Entec Polymers |
| Trademark: | Hyrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ddUDHa_Hyrene-PS-HI-3-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hyrene® PS-HI 3/4 is a High Impact Polystyrene material. It is available in North America. Important attributes of Hyrene® PS-HI 3/4 are:
Typical application of Hyrene® PS-HI 3/4: Food Contact Applications |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.7 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, Injection Molded) | 22.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C, Injection Molded) | 60 | % | ASTM D638 |
| Flexural Modulus (23°C, Injection Molded) | 2020 | MPa | ASTM D790 |
| Flexural Strength (23°C, Injection Molded) | 39.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 77.8 | °C | ASTM D648 |
| Vicat Softening Temperature | 96.7 | °C | ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207 C | RTP Company | Nylon 11 | RTP |
| TUFNYL® RGF 10 BLUE | SRF Ltd. | Nylon 66 | TUFNYL® |
| Anjaflam® 100X-FR/UV | Almaak International GmbH | PC | Anjaflam® |
| LEXAN™ EXL1112T resin | SABIC Innovative Plastics | PC | LEXAN™ |
| ESTOPLAST EP 5010GN29 | Ester Industries Ltd. | PBT | ESTOPLAST EP |