Multilon® TN-7570Z
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Multilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ddAcgR_MultilonTN7570Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS polymer alloy, Non-halogen type flame resistant series |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Transverse flow : 4.00mm | 0.50 - 0.70 | % | Internal method |
| Flow : 4.00mm | 0.50 - 0.70 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 65.0 | MPa | ISO 527-2/50 |
| Fracture | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 3.0 | % | ISO 527-2/50 |
| Fracture | 45 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2800 | MPa | ISO 178 |
| Flexural Stress 2 | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 91.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 94.0 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | V-0 | UL 94 | |
| 2.0 mm | 5VB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4MID® 9A22115 | 4Plas | Nylon 66 | 4MID® |
| 3M™ Dyneon™ Fluoroplastic PFA 6502TZ | 3M Advanced Materials Division | PFA | 3M™ Dyneon™ Fluoroplastic |
| GELAST 5170A | Guang Sung Plastics (GSPL) | ABS | GELAST |
| MAJORIS BW300 - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| TAFMER™ H-1030S | Mitsui Chemicals, Inc. | PAO | TAFMER™ |