LNP™ LUBRICOMP™ LL004C compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dcbl85_LNPLUBRICOMPLL004Ccompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP LL004C is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated, Clean Compounding System. Also known as: LNP* LUBRICOMP* Compound LL-4040 CCS Product reorder name: LL004C |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 1.3 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.9 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.9 | % | ISO 294-4 |
| Flow direction : 24 hours | 1.3 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2900 | MPa | ASTM D638 |
| -- | 3070 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 74.5 | MPa | ASTM D638 |
| Yield | 73.0 | MPa | ISO 527-2 |
| Fracture | 69.6 | MPa | ASTM D638 |
| Fracture | 69.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.8 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2 |
| Fracture | 23 | % | ASTM D638 |
| Fracture | 12 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2960 | MPa | ASTM D790 |
| -- | 3320 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 117 | MPa | ASTM D790 |
| -- | 118 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.52 | ASTM D3702 Modified | |
| With Self-Static | 0.43 | ASTM D3702 Modified | |
| Wear Factor - Washer | 128 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 2 | 8.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1500 | J/m | ASTM D4812 |
| 23°C 3 | 91 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 3.00 | J | ASTM D3763 |
| -- | 1.00 | J | ISO 6603-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8204-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Mylar® D1 (1000 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| NOVADURAN® SEF-530X | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| Fainplast PVC GS 69/T | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Karina GREEN COLOR CONCENTRATE 40/257-FC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |