Flexirene® CL 10 F
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Flexirene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | daGGMn_Flexirene-CL-10-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flexirene CL 10 is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for cast extrusion of thin film with high optical properties. Main Application Flexirene CL 10 is recommended for the production of stretch film to be used both in manual and in automatic wrapping machines. In a multilayer film, Flexirene CL 10 enhances the optical properties of the global formulation; moreover, for its high processability, the resin is recommended whenever high productivity has to be reached. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.8 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Cast Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Film Thickness - Recommended / Available | 10 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 23 µm, Cast Film | 90.0 | MPa | |
| 1% Secant, TD : 23 µm, Cast Film | 105 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 23 µm, Cast Film | 9.00 | MPa | |
| TD : Yield, 23 µm, Cast Film | 8.00 | MPa | |
| MD : Break, 23 µm, Cast Film | 35.0 | MPa | |
| TD : Break, 23 µm, Cast Film | 25.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 23 µm, Cast Film | 600 | % | |
| TD : Break, 23 µm, Cast Film | 800 | % | |
| Dart Drop Impact 1(23 µm, Cast Film) | 100 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 23.0 µm | 38.0 | kN/m | |
| TD : 23.0 µm | 103.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 97.0 | °C | ISO 306/A |
| Melting Temperature | 121 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 23.0 µm, Cast Film) | 91 | ASTM D2457 | |
| Haze (23.0 µm, Cast Film) | 2.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 to 270 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP240H | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Vibrathane® B836 | Chemtura | PUR-Ether/MDI | Vibrathane® |
| Ferro PP LPP40BK06NA | Ferro Corporation | PP, Unspecified | Ferro PP |
| Latan 13 S/15 | LATI S.p.A. | Acetal (POM) Copolymer | Latan |
| Karina IVORY PVC COMPOUND 75850-35/ 1-F-AC-LF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |