HiFill® PA6/6,6 GF30 IM2 HS L
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dZCUYG_HiFill-PA6-6-6-GF30-IM2-HS-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill®PA6/6,6 GF30 IM2 HS L is a polyamide 66 (nylon 66) product, which contains a 20% glass fiber reinforced material. It can be processed by injection molding and is available in North America. The main characteristics are: lubrication. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.35 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.88 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 145 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus | 8270 | MPa | ASTM D790 |
| Flexural Strength | 234 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 150 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 180 | J/m | ASTM D256 |
| Unnotched Izod Impact | 1400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 263 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 232 | °C | ASTM D648 |
| CLTE - Flow | 3.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 15 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Rear Temperature | 282 - 293 | °C | |
| Middle Temperature | 288 - 299 | °C | |
| Front Temperature | 277 - 288 | °C | |
| Nozzle Temperature | 282 - 293 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 54.4 - 93.3 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well ventedMoisture Content, as received: Product is packaged at 0.2% or less.Recomended Max Moisture: 0.12% down to 0.08% |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VAMPAMID 66 3054 V0 | Vamp Tech | Nylon 66 | VAMPAMID |
| Geon™ Vinyl Flexible XV3902 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| ELASTOSIL® R plus 4060/50 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| LOXIM 820 02C HB | LOXIM Industries Private Limited | PP, Unspecified | LOXIM |
| 3M™ Dyneon™ Fluoroelastomer FC 2179 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |