POLYFLAM® RPP 4000 E Datasheet,PP Homopolymer,A. Schulman Europe-SHANGHAI SUSHENG

Message
Unfilled flame-retardant PP-Homopolymer, Extrusion grade, halogenfree

General Information
Features	Homopolymer Workability, good Halogen-free Flame retardancy
Processing Method	Extrusion Injection molding
Resin ID (ISO 1043)	PP FR(51)

Physical	Nominal Value	Unit	Test Method
Density	1.06	g/cm³	ISO 1183/A
Melt Volume-Flow Rate (MVR) (230°C/2.16 kg)	2.00	cm³/10min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2600	MPa	ISO 527-2/1A/1
Tensile Stress			ISO 527-2/1A/50
Yield	26.8	MPa	ISO 527-2/1A/50
Fracture	16.6	MPa	ISO 527-2/1A/50
Tensile Strain (Yield)	4.1	%	ISO 527-2/1A/50
Nominal Tensile Strain at Break	26	%	ISO 527-2/1A/50
Flexural Modulus ¹	2300	MPa	ISO 178
Flexural Stress ²			ISO 178
5.1% strain	39.0	MPa	ISO 178
3.5% strain	37.1	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	1.5	kJ/m²	ISO 179/1eA
23°C	2.5	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	15	kJ/m²	ISO 179/1eU
23°C	40	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	108	°C	ISO 75-2/B
1.8 MPa, not annealed	58.0	°C	ISO 75-2/Af
Vicat Softening Temperature
--	154	°C	ISO 306/A50
--	97.0	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flammability Classification			IEC 60695-11-10, -20
0.8 mm	V-0		IEC 60695-11-10, -20
1.6 mm	V-0		IEC 60695-11-10, -20
3.2 mm	V-0		IEC 60695-11-10, -20
3.0 mm	5V 5VA		IEC 60695-11-10, -20
Glow Wire Flammability Index			IEC 60695-2-12
0.75 mm	960	°C	IEC 60695-2-12
1.5 mm	960	°C	IEC 60695-2-12
3.0 mm	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature			IEC 60695-2-13
0.75 mm	775	°C	IEC 60695-2-13
1.5 mm	775	°C	IEC 60695-2-13
3.0 mm	775	°C	IEC 60695-2-13

Additional Information
1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications

Injection	Nominal Value	Unit
Drying Temperature	70	°C
Drying Time	2.0 - 4.0	hr
Processing (Melt) Temp	180 - 210	°C
Mold Temperature	40 - 80	°C
Injection Pressure	80.0 - 120	MPa
Injection Rate	Slow-Moderate
Holding Pressure	40.0 - 90.0	MPa
Back Pressure	5.00 - 10.0	MPa
Screw Speed		mm/sec

Injection instructions
PredryingPredrying at 70°C for 2-4 hours is recommended as a precaution.ReprocessingAddition of regrind is normally possible, but it must be tested in each case regarding the percentage and requirements of the article. Thermal damage during first processing depends on processing parameters and the geometry of flow path and article.Shut downAvoid long melt residence time. Purge with base polymer or with polyolefines.FinishingMachining is usually possible.

Injection instructions

PredryingPredrying at 70°C for 2-4 hours is recommended as a precaution.ReprocessingAddition of regrind is normally possible, but it must be tested in each case regarding the percentage and requirements of the article. Thermal damage during first processing depends on processing parameters and the geometry of flow path and article.Shut downAvoid long melt residence time. Purge with base polymer or with polyolefines.FinishingMachining is usually possible.

Note Message
1 .	2.0 mm/min
2 .	2.0 mm/min

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	A. Schulman Europe
Trademark:	POLYFLAM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	dXo2Zt_POLYFLAMRPP4000E.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 382 TFE 5	RTP Company	PC	RTP
TEKANATE™ G730FR	Mando Advanced Materials Co., Ltd.	PC	TEKANATE™
SUMIKASUPER® LCP E6007LHF	Sumitomo Chemical Co., Ltd.	LCP	SUMIKASUPER® LCP
Tenopom® POM B3 MF PRTA011 PR305 MSP	Petropol Industry and Trade of Polymers LTDA	Acetal (POM) Copolymer	Tenopom® POM
Yanshan PE 7000F	SINOPEC Beijing Yanshan Petrochemical	HDPE	Yanshan PE