UmaPET TFMH

Category:	PET , Polyethylene Terephthalate
Manufacturer:	Ester Industries Ltd.
Trademark:	UmaPET
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	dVmRXS_UmaPET-TFMH.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

KEY FEATURES

UmaPET TFMH is high barrier metallized film, metallized on plain surface with plasma, other side plain. It exhibits good barrier properties along with good metal to film bond strength/adhesion.

It has excellent mechanical properties, flex crack resistance and excellent gloss.

APPLICATIONS

UmaPET TFMH is used as sandwich barrier layer in flexible packaging applications which require good barrier and good bond strength in laminates.

Typical usage as barrier layer in laminates for confectionary, milk powder, cereals, juice powder, snacks, chips, extruded foods, tea etc.

General Information
Features	Barrier Resin Bondability Good Adhesion Good Crack Resistance High Gloss Metallizable
Uses	Film Laminates Packaging
Forms	Film

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage			ASTM D1204
Flow : 150°C, 30 min, 0.0100 mm	2.5	%
Flow : 150°C, 30 min, 0.0120 mm	2.5	%
Across Flow : 150°C, 30 min, 0.0100 mm	0.40	%
Across Flow : 150°C, 30 min, 0.0120 mm	0.40	%
Surface Tension - Metallized side			ASTM D2578
10.0 µm	56	mN/m
12.0 µm	56	mN/m

Films	Nominal Value	Unit	Test Method
Yield			Internal Method
10.0 µm	71.4	m²/kg
12.0 µm	59.5	m²/kg

Optical	Nominal Value	Unit	Test Method
Optical Density			Internal Method
10.0 µm	-2.4 to 7.6	%
12.0 µm	-2.4 to 7.6	%

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	10 12	µm
Film Thickness - Recommended / Available	10, 12 µm
Tensile Strength			ASTM D882
MD : Break, 10 µm	206	MPa
MD : Break, 12 µm	206	MPa
TD : Break, 10 µm	216	MPa
TD : Break, 12 µm	216	MPa
Tensile Elongation			ASTM D882
MD : Break, 10 µm	100	%
MD : Break, 12 µm	100	%
TD : Break, 10 µm	90	%
TD : Break, 12 µm	90	%
Oxygen Permeability ¹			ASTM D3985
23°C, 10 µm	0.700	cm³/m²/24 hr
23°C, 12 µm	0.800	cm³/m²/24 hr
Water Vapor Transmission			ASTM F1249
-- ²	0.40	g/m²/24 hr
-- ³	0.50	g/m²/24 hr

Note Message
1 .	0%RH
2 .	37.8°C, 90%RH, 10 µm
3 .	37.8°C, 90%RH, 12 µm

Resin Grade	Manufacturer	Category	Trademark
TAIRIPRO T2502	Formosa Plastics Corporation	PP Homopolymer	TAIRIPRO
Tarnamid® T- 27 CF10	Grupa Azoty S.A.	Nylon 6	Tarnamid®
ESENTTIA 01H41	Polipropileno del Caribe S.A.	PP Homopolymer	ESENTTIA
HiFill® PBT GF40	Techmer Engineered Solutions	PBT	HiFill®
SABIC® PPcompound 8250U	Saudi Basic Industries Corporation (SABIC)	PP, Unspecified	SABIC® PPcompound