CERTENE™ LLMF-118A
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dVHYn8_CERTENE-LLMF-118A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LLMF-118A is a certified prime resin designed for production of Blown films needing excellent optics, superior film strength and excellent heat seal performance. LLMF-118A applications include heavy duty packaging, ice bags and sealant layer in coextrusions. LLMF-118A contains no slip, no antiblock and does contain process aid. LLMF-118A complies with FDA regulation 21CFR 177.1520(c)3.2a, conditions of use B-H. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm | 175 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm | 191 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 10.7 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 9.65 | MPa | ASTM D882 |
| MD : Break, 25 µm | 58.6 | MPa | ASTM D882 |
| TD : Break, 25 µm | 51.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 450 | % | ASTM D882 |
| TD : Break, 25 µm | 600 | % | ASTM D882 |
| Dart Drop Impact 1(25 µm) | 800 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 230 | g | ASTM D1922 |
| TD : 25 µm | 500 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 25.4 µm, Blown Film) | 130 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 4.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film Specimen: 1.0 mils (25 µm) film; blow-up-ratio 2.5 :1; Melt temperature 400°F |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 204 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ProvaMed® PVC 5377 | ACTEGA GmbH | PVC, Unspecified | ProvaMed® PVC |
| S&E PVC GA-1008 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| ULTEM™ STM1600 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Badaflex® TPE-S 30A 1000 | Bada AG | TPE | Badaflex® |
| POLIMAXX 1175SM | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |