Hanwha Total PE 620A
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dQLQyN_Hanwha-Total-PE-620A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 620A is a low-density polyethylene resin for non-crosslinked foam sheet applications. This grade is for conventional extrusion and foaming process. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 12.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 680 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 87.0 | °C | ASTM D1525 1 |
| Melting Temperature | 109 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 190 to 210 | °C | |
| Cylinder Zone 2 Temp. | 190 to 210 | °C | |
| Cylinder Zone 3 Temp. | 120 to 150 | °C | |
| Cylinder Zone 4 Temp. | 120 to 150 | °C | |
| Die Temperature | 105 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 B | RTP Company | Nylon 610 | RTP |
| Pomalux® Unfilled | Westlake Plastics Company | Acetal (POM) Copolymer | Pomalux® |
| Titalon® 4115CF | Titan Plastics Compounds Co., Ltd. | Nylon 46 | Titalon® |
| Karina CLEAR PVC COMPOUND 80/204-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Mitsui EPT™ 3062EM | Mitsui Chemicals, Inc. | EPDM | Mitsui EPT™ |