Hyundai EP Adhesives HB520/1002
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | HYUNDAI EP Co., Ltd. |
| Trademark: | Hyundai EP Adhesives |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dPmmlg_Hyundai-EP-Adhesives-HB520-1002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hyundai EP Adhesives HB520/1002 is a Polyethylene product. It is available in Asia Pacific. Applications of Hyundai EP Adhesives HB520/1002 include adhesives/tapes and bottles. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.956 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Water Absorption (24 hr) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 29.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 630 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Adhesion Strength | > 2.0 | kN/m | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Akulon® S227-C | DSM Engineering Plastics | Nylon 66 | Akulon® |
| DOW™ Electrical & Telecommunications DFDA-1375 RD | The Dow Chemical Company | LLDPE | DOW™ Electrical & Telecommunications |
| Hylon® N2213STHL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| POLYFORM C 27 natural | POLYMA Kunststoff GmbH & Co. KG | Acetal (POM) Homopolymer | POLYFORM |
| ESTOPLAST XU 230HSNN01 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |