InnoTuf® TP-4045
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTuf® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dOgvfY_InnoTuf-TP-4045.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TP-4045 is an impact resistant polyurea formulated for room temperature hand-batch or machine dispensable systems. Excellent physical properties can be obtained without the utilization of mercury, MOCA, or TDI. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Base Resin | 1.16 | g/cm³ | |
| Cured | 1.18 | g/cm³ | |
| Hardener | 1.24 | g/cm³ | |
| Molding Shrinkage - Flow | 0.20 to 0.80 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 758 | MPa | ASTM D790 |
| Flexural Strength | 24.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 350 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 85.0 | °C | |
| 1.8 MPa, Unannealed | 74.0 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 50 Mix Ratio by Weight: 53 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 60 to 120 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 38°C 1 | 0.10 | Pa·s | |
| 38°C 2 | 2.1 | Pa·s | |
| 38°C 3 | 5.1 | Pa·s | |
| Curing Time (25°C) | 1.7E+2 | hr | |
| Gel Time | 4.0 to 6.0 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 65 to 75 | ASTM D2240 | |
| Tensile Strength | 27.6 | MPa | ASTM D638 |
| Tensile Elongation at Break | 70 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ HDPE 8262B | The Dow Chemical Company | HDPE | DOW™ HDPE |
| ACCUTECH™ HP0339W40L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Amodel® AS-1145 HS | Solvay Specialty Polymers | PPA | Amodel® |
| Haysite BMC 14200 | Haysite Reinforced Plastics | Polyester, TS | Haysite BMC |
| HiFill® HDPE GF15 50100 | Techmer Engineered Solutions | HDPE | HiFill® |